Ceramic coatings could protect jet engines from volcanic ash

A new class of ceramic coatings could offer jet engines special protection against volcanic ash damage.

Researchers from Ohio State University tested two coatings that were originally developed to keep airborne sand from damaging jet engines and found that the coatings also resist damage caused by ash deposits.

‘We determined that these coatings could offer sufficient protection against small amounts of ash ingested by the engine over time,’ said Prof Nitin Padture from the College of Engineering at Ohio State University, who led the study.

However, large amounts of ash can temporarily jam a jet engine and cause it to stall, he explained. These coatings would not be useful in those extreme circumstances.

Temperatures inside an engine reach up to 2,500°F and ceramic thermal-barrier coatings insulate metallic engine parts from that heat. The ingested ash melts onto the coating and penetrates it. As it cools, the molten ash forms a brittle glass that flakes off, taking the coating with it.


When the Icelandic volcano Eyjafjallajökull erupted in April 2010, it billowed clouds of silicate ash.

‘Ash composition varies widely depending on the type of volcano. After what happened in Iceland, we wanted to see how ash interacted with our new thermal barrier coating and whether the underlying damage mechanisms were any different,’ he said.

Doctoral students Julie Drexler and Andrew Gledhill took samples of the ceramic coatings on pieces of metal and coated them with ash from the Eyjafjallajökull eruption. Then they heated the samples in a furnace to simulate the high temperatures created in a jet engine.

They experimented with a typical jet-engine coating and two sand-resistant coatings. One was Padture’s formula, containing zirconia and alumina, and the other was a commercially available new formula based on gadolinium zirconate.

In that test, the ash badly damaged the typical coating, while coatings made of Padture’s formula and the gadolinium-zirconate formula retained their overall structure.

Looking at cross-sections of the samples, the researchers saw that molten ash had penetrated through the pores of the typical ceramic coating all the way to its base. But in the other two, the molten ash barely penetrated.

‘Pores give the coating its strain tolerance,’ said Drexler. ‘They make room for the coating to expand and contract as the engine heats up while flying, and as it cools after landing. When all the pores are plugged with ash, the coating can’t adjust to the temperature anymore and it breaks off.’

On the sand-resistant coatings, the ash filled the pores only near the surface. Chemical analysis revealed that the ash reacted with the alumina in the first coating to produce a thin layer of the mineral anorthite below the surface, while, on the gadolinium zirconate, it produced a layer of the mineral apatite.

‘The chemical reaction arrests the penetration of the ash into the coatings,’ Gledhill said. ‘The unaffected pores allow the coating to expand and contract.’


Now, the researchers are repeating their experiment with a new setup. They are heating samples repeatedly with a powerful blowtorch and letting them cool in between to more closely simulate engine conditions.

Both sand-resistant coatings are more expensive than the typical coating, but the researchers think that the benefits outweigh the cost.

‘This study’s not going to solve all the problems of ash clouds and jet engines, but we are making progress and we’ve learnt a lot about the physics of the situation,’ Padture said.

The study is published online in the ’Early View’ edition of the journal Advanced Materials.